Fabrication of Fluorine-Free Superhydrophobic Surface on Aluminum Substrate for Corrosion Protection and Drag Reduction

Abstract

A fluorine-free cerium palmitate superhydrophobic surface on an aluminum plate was fabricated via a two-step electrodeposition method. The mechanical durability, anti-corrosion performance, water repellency and drag reduction properties were tested. The results indicate that a superhydrophobic surface with a densely packed convex island shape with micro-pores and nano-scale strips was formed on the aluminum plate. Furthermore, the as-prepared surface exhibits excellent water-repelling ability with a water contact angle of 162.3° and a sliding angle of 1.5°. Owing to the protective effect of the convex island structure on the surface, the surface also shows superb mechanical durability, which is a shortcoming of ordinary electrodeposited surfaces. Moreover, compared with bare aluminum, the corrosion inhibition efficiency of the superhydrophobic surface is 99.55% and the surface drag decreases by 65.3% at a lower flow rate. Therefore, it is believed that the environmentally friendly fluorine-free superhydrophobic surface has promising potential applications in marine engineering.

Bibliographic Information