Impact of diatomite addition on lead immobilization in air pollution control residues from a municipal solid waste incinerator

Abstract

Air pollution control (APC) residues, which are known to be the byproducts of incineration treatment, exhibit a high leaching potential of toxic metals. Calcium silicate hydrate (C-S–H), which is a major hydration product of hardened cement and immobilizes toxic metal, can be formed by the reaction of Ca with pozzolanic Si in a highly alkaline environment. Toxic metals might be immobilized by the addition of pozzolanic material to APC residues (instead of using cement), which is a Ca source and provides an alkaline condition. In this study, diatomite, which mainly comprises amorphous silica (SiO 2 ·nH 2 O), was investigated as a pozzolanic material for Pb immobilization in APC residues obtained from a municipal solid waste incinerator. APC residues were cured with and without the addition of diatomite at different temperatures. When diatomite was added to APC residues, pozzolanic phases such as C-S–H gel were formed via the consumption of Ca(OH) 2 and CaClOH. Compared to APC residues cured without diatomite, the leaching of Pb decreased by 99% for APC residues cured for 14 days with 10% diatomite at 70 °C. The results of sequential chemical extraction showed that water-soluble Pb in APC residues was reduced from 10.3% to nearly zero by the pozzolanic reaction. Consequently, the leaching amount of Pb dropped below 0.3 mg/L (Japanese criteria for landfill disposal). Overall, these experiments provide promising results regarding the possibility of using diatomite for pretreating APC residues.

Bibliographic Information