Graphene-based versus alumina supports on CO2 methanation using lanthanum-promoted nickel catalysts

Abstract

The valorization of CO 2 as a biofuel, transforming it through methanation as part of the power-to-gas (P2G) process, will allow the reduction of the net emissions of this gas to the atmosphere. Catalysts with 13 wt.% of nickel (Ni) loading incorporated into alumina and graphene derivatives were used, and the effect of the support on the activity was examined at temperatures between 498 and 773 K and 10 bar of pressure. Among the graphene-based catalysts (13Ni/AGO, 13Ni/BGO, 13Ni/rGO, 13Ni-Ol/GO, 13Ni/Ol-GO, and 13Ni/Ol-GO Met), the highest methane yield was found for 13Ni/rGO (78% at 810 K), being the only system comparable to the catalyst supported on alumina 13Ni/Al 2 O 3 (89.5% at 745 K). The incorporation of 14 wt.% of lanthanum (La) into the most promising supports, rGO and alumina, led to nickel-support interactions that enhanced the catalytic activity of 13Ni/Al 2 O 3 (89.5% at lower temperature, 727 K) but was not effective for 13Ni/rGO. The resistance against deactivation by H2S poisoning was also studied for these catalysts, and a fast deactivation was observed. In addition, activity recovery was impossible despite the regeneration treatment carried out over catalysts. The resistance against deactivation by H2S poisoning was also studied for these catalysts, observing that both suffered a rapid/immediate deactivation and which in addition/unfortunately was impossible to solve despite the regeneration treatment carried out over catalysts.

Bibliographic Information